Properties Of HighÂlime Fly Ash Concrete :: Concrete

PROPERTIES OF HIGHLIME FLY ASH CONCRETEABSTRACTFly modify is a waste product from burn based thermal power stations. About seven million tons of fly ash is being produced annually from these thermal power stations in Turkey. Concerted efforts are needed to make the material used to a great extent.These paper give the results of an investigation on the performance of fly ash concrete made with ASTM C class fly ashes from two sources. PC42,5 cement used in the experiments conforms to TS19 (Turkish Standards).A comparison between concretes with and without fly ash was provided for heterogeneous aspects. All the concrete mixtures contained polyhydroxy carbon salt plasticizer which complies with ASTM C 494-81 Type D. Their workabilities were kept constant.As freshly-mixed concrete properties slump, unit weight, air content, setting time and release values were determined.As mechanical properties compressive strength and were measured after 24 hours, 7, 28 and 90 days.Durability in te rms of freezing and thawing apology (ASTM C 666 Procedure A), and permeability were also investigated.Keywords Fly ash, concrete properties, binder material, micro-structureSenel Artirma, Geophysics Engineer, Quality Assurance Manager of Nuh Beton Ready-Mixed Concrete Company, Turkey.Erdem Tandirli, Civil Engineer, Quality authorization Chief of Nuh Beton Ready-Mixed Concrete Company, Turkey.11. INTRODUCTIONEnvironmental hazards and over-comsumption of energy resources has been and still are the most concerning issues for the modern world. In this respect the usage of fly ash which is a waste product of the thermal power stations by ready-mixed concrete industry as a binder material can be an effective way both of decreasing the ash discharge out to the environment and of cement consumption thus of saving the resources on a guinea pig scale.From the concrete technologys point of view, the usage of fly ash causes qualitative changes in concrete properties. The answer to whether th ese changes were improvement or not can be given(p) only by knowing the intentions of usage.For this purpose fly ashes were added both in addition to and as a substitute for some part of the cement, and fresh and treated concrete properties were investigated.2. EXPERIMENTAL STUDIES2.1 Materials2.1.1 CementThe cement used is Turkish, portland cement (PC 42.5) and comforms to Turkish standart TS19 while approximately corresponds to ASTM C 150-89 Type I. Its chemical composition, and principal compounds are summarized in Table 1.a, physical and mechanical properties in Table 1.b along with standart limits.Table 1.a Chemical properties of cementChemical CompositionComponents, %PC 42.5TS 19ASTM Type ISiO221.16--Al2O33.60--Fe2O34.50--CaO64.90--MgO1.205 max.